Zirconite

Zirconite

Dual-cure permanent adhesive resin cement designed for Zirconia

• Permanent cementation of Ceramic and Zirconia restorations
• Proven Color Stability over time.

An innovative dual-cure permanent adhesive resin cement specially formulated for Zirconia cementation

• ISO 4049 classification: Type 2, Class 3.
• Self-etch, self-adhering, dual cured, radiopaque permanent resin cement that does not require etching, priming, or bonding.
• Radiopacity value above 2.5 mm Aluminium. (Radiopacity is defined as the ability of a material to be visible in x-ray photographs.)
• Chemical affinity for metal and Zirconia.
• Dual-cure cement – it has a self curing mechanism which can also be light cured for an immediate set and extra strength at the margins.
• Features high retention and total margin integrity.
• Administration via Automix syringe saves application time and guarantees consistent mix.
• Available in 3 shades: Dentin, Translucent, White, To see shade guide visit www.bjmlabs.com.
• Marketed since 2009. No complaints of any health-related or chemical performance issues were received.

Technical Data

Compressive strength: > 150 MPa

Flexural strength: > 100 MPa

Water sorption: ≤ 40 μg/mm3

Solubility: ≤ 7.5 μg/mm3

Shear bond strength to etched enamel: > 10 MPa

Shear bond strength to un-etched dentin: > 5 MPa

Shear bond strength to pretreated metal alloy: > 10 MPa

Shear bond strength to un-treated ceramic surface (Zirconia): > 5 MPa

Film thickness: <50

Radiopacity: >100 % Al

Working time (in ambient light and temperature): > 90 seconds, in the 1.5 - 3.5 min interval

Setting time (in oral temperature): < 10 minutes, in the 2.5 - 4.5 min interval

Light curing time: 10 – 20 seconds

Compatible with LED: Yes

Compatible with halogen light: Yes

Compatible with plasma ark light lamp: Yes

Shelf life: 2 Years